PRIMASELECT LUVOCOM 3F PEKK 50082 - 1.75MM - 500G - NATURAL

PrimaSELECT™ Luvocom 3F 9581 PEKK (polyether-ether-ketone) is a semi-crystalline thermoplastic material. 3D print this high-performance plastic with your 3D printer today. PEKK has high resistance to heat, chemicals, and mechanical stress. Therefore, it is used to produce parts for the aerospace, gas, oil, medical, and automotive industries.

Properties of PrimaSELECT™ Luvocom 3F 9581 PEKK material:

• Specially optimized for industrial 3D printing – Isotropic shrinkage characteristics
• Non-flammable (UL94 V-0) and highly chemical resistant
• Continuous service temperature of 255°C – Service temperature 300°C (for max. 200 hours lifetime)
• Low warp

Buy PEKK 3D printer filament for applications with maximum performance

Polyetherketoneketone (PEKK) is a semi-crystalline thermoplastic material. It belongs to the polyaryletherketone family. Due to its high heat and chemical resistance and the ability to withstand high mechanical loads, it is perfect for manufacturing demanding end-use parts. Moreover, it is inherently flame retardant and features unique tribological properties.

Properties of PrimaSELECT™ Luvocom 3F 9581 PEKK material:

• Specially optimized for industrial 3D printing
• Isotropic shrinkage characteristics
• Non-flammable (UL94 V-0)
• Continuous service temperature 255°C
• Service temperature 300°C (for max. 200 hours lifetime)
• Highly chemical resistant
• Low warp PEKK filament

PEKK is easier to process than PEEK filament

PEKK filament has an adjustable crystallization rate that allows FFF or FDM 3D printer users to exploit both the extreme performance of PEEK and the easier processing of amorphous materials. PEKK filament is easier to process than traditional PEEK filament and has better layer adhesion. At the same time, it offers similar strength and resistance material properties and better dimensional stability. PEKK has a higher glass transition temperature than PEEK by 15ᵒC.

LUVOCOM® 3F PEKK 50082 material properties:

• Density 1.27 g/cm³
• Tensile strength 90 MPa
• Elongation at max. force 5%
• Elastic modulus 3 GPa
• Flexural strength 150 MPa
• Elongation at flexure at max. force 6%
• Flexural modulus 2.5 GPa

3D print PEKK with low warp

LUVOCOM® 3F PEKK 50082 is designed to outperform standard PEKK materials on the market. It features improved flow characteristics that improve processing and layer adhesion. This unique modified pure PEKK offers dimensional stability and can be processed in unheated build chambers, yielding semi-crystalline parts with low warp.

3D printing settings:

• Print temperature: 340°C (320-360°C
• Bed temperature: 110-140°C
• Print speed: 20-50 mm/s
• Drying instructions: 4 hours, 110°C